Model No: ASTM A213
Marka: TORICH
Packaging: W wiązkach W drewnianych pudełkach
wydajność: 60000 Tons per Year
transport: Ocean,Land,Air
Place of Pochodzenia: Chiny
Wsparcie: 60000 Tons per Year
Certyfikat: ISO 9001 ISO 14001 TS 16949 EN 10204.3.1 LR KR
Código HS: 7304419000
Porta: Ningbo,Shanghai
Rodzaj płatności: L/C,T/T,D/P,Paypal,Money Gram,Western Union
Incoterm: FOB,CFR,FCA,CPT
Anodowana stalowa bezszwowa rura marynowana do kotła
Product Name | ASTM A213 316Ti stainless steel seamless tube |
Material | stainless steel 316Ti |
Process | cold drawn, cold rolling |
Standard | A213, A312, A269, A511 |
Grade | 304, 304L, 316L, 321, 347H, S31803, 904L |
Size | 6 - 610 mm |
Length | 800mm - 20000 mm |
Used | bolier, heat exchanger |
Tolerancja dla bezszwowej rury kotła ze stali nierdzewnej:
Production Method | Size(mm) | Tolerance | |
Hot Rolling(Extrusion) | OD | ≤140 | ±1.25% |
>140 | ±1.0% | ||
WT | ≤10 | ±12.5% | |
>10 | ±15% | ||
Cold Drawn(Cold Rolled) | OD | 8~30 | ±0.20mm |
>30~50 | ±0.30mm | ||
>50 | ±0.8% | ||
WT | 1.0~3 |
+12% -10% |
|
>3.0 |
±10% |
Standard | ASME SA213/ASTM A213, ASTM A269/ASME SA269, ASME SA312/ASTM A312, ASME249/ASTM A249, ASME SA511/ASTM A511, ASTM A270/ASME SA270, EN10216-5,EN10305-1, EN10217-5, DIN 17175, DIN 2448, DIN 6258, GOST 8731, JIS G3463, JIS G3462, JIS G3455, JIS G3459 etc. |
Material | TP304, TP304L, TP304H, TP304LN, TP314, TP316, TP316L, TP316LN, TP321, TP321H, TP310, TP310S, TP317, TP317L, TP347, TP347H, N08904, 904l, 253MA(S30815), 254SMO(S31254). |
Type | Seamless / SML |
O.D | 6-530mm |
W.T | 0.7-50mm |
Length | 0-38000mm |
Technique | Cold Finished (Cold Drawing and Cold Rolling), Hot Finished (Hot Extrusion) |
Ends | PE/Plain Ends, BE/Beveled Ends |
Zakresy składu dla stali nierdzewnej 316 .
Grade |
|
C | Mn | Si | P | S | Cr | Mo | Ni | N |
---|---|---|---|---|---|---|---|---|---|---|
316 | Min | - | - | - | 0 | - | 16.0 | 2.00 | 10.0 | - |
Max | 0.08 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
316L | Min | - | - | - | - | - | 16.0 | 2.00 | 10.0 | - |
Max | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
316H | Min | 0.04 | 0.04 | 0 | - | - | 16.0 | 2.00 | 10.0 | - |
max | 0.10 | 0.10 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | - |
Właściwości mechaniczne stali nierdzewnej 316.
Grade | Tensile Str (MPa) min | Yield Str 0.2% Proof (MPa) min | Elong (% in 50 mm) min | Hardness | |
---|---|---|---|---|---|
Rockwell B (HR B) max | Brinell (HB) max | ||||
316 | 515 | 205 | 40 | 95 | 217 |
316L | 485 | 170 | 40 | 95 | 217 |
316H | 515 | 205 | 40 | 95 | 217 |
Typowe właściwości fizyczne stali nierdzewnej 316 .
Grade | Density(kg/m3) | Elastic Modulus (GPa) | Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat 0-100 °C (J/kg.K) | Elec Resistivity (nΩ.m) | |||
---|---|---|---|---|---|---|---|---|---|
0-100 °C | 0-315 °C | 0-538 °C | At 100 °C | At 500 °C | |||||
316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Specyfikacja gatunku dla stali nierdzewnej 316 .
Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
---|---|---|---|---|---|---|---|
BS | En | No | Name | ||||
316 | S31600 | 316S31 | 58H, 58J | 1.4401 | X5CrNiMo17-12-2 | 2347 | SUS 316 |
316L | S31603 | 316S11 | - | 1.4404 | X2CrNiMo17-12-2 | 2348 | SUS 316L |
316H | S31609 | 316S51 | - | - | - |
Właściwości mechaniczne
Obróbka cieplna podłużnych właściwości mechanicznych rur stalowych powinna być zgodna z normą.
Material |
Tensile strength MPa ≥ |
Yield Strength MPa ≥ |
Elongation % ≥ |
0Cr18Ni9 | 520 | 205 | 35 |
1Cr19Ni9 | 520 | 205 | 35 |
0Cr19Ni10 | 480 | 175 | 35 |
1Cr18Ni9Ti | 550 | 205 | 40 |
0Cr18Ni12Mo2Ti | 530 | 205 | 35 |
0Cr26Ni5Mo2 | 590 | 390 | 18 |
1Cr17 | 410 | 245 | 20 |
00Cr27Mo | 410 | 245 | 20 |
1Cr25Ti | 440 | 245 | 17 |
Twardość:
W przypadku rur WT ≥ 2 mm należy wykonać testy twardości Rockwella.
Testy rur kotła bez szwu:
1. Test gięcia:
Probówki powinny wykonać próbę zginania, gdy OD ≤22 mm. Kąt gięcia wynosi 90 stopni, a promień gięcia jest 6 razy większy od zewnętrznej średnicy stalowej rury.
2. Test hydrauliczny;
Badania prądów wirowych, badania ultradźwiękowe mogą być stosowane zamiast testów hydraulicznych. Podczas badania prądów wirowych, GB / T 7735-1995 Gr. Należy przestrzegać; gdy badania ultradźwiękowe, GB / T 5777-1996 Gr. Należy przestrzegać C8.
3. Test spłaszczania
4. Test obwisania
5. Rozwiń test
Kategorie o produkcie : Rury stalowe bez szwu
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.